性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
密度 | ASTM D-1505 | 0.928 | g/cm3 | |
熔体流动速率 | ASTM D-1238 | 1 | g/10min | |
拉伸屈服强度(MD) | ASTM D-882 | 165 | Kg/cm2 | |
拉伸屈服强度(TD) | ASTM D-882 | 150 | Kg/cm2 | |
拉伸断裂强度(MD) | ASTM D-882 | 590 | Kg/cm2 | |
拉伸断裂强度(TD) | ASTM D-882 | 530 | Kg/cm2 | |
伸长率(MD) | ASTM D-882 | 700 | % | |
伸长率(TD) | ASTM D-882 | 800 | % | |
撕裂强度(MD) | ASTM D-1922 | 10 | g/m | |
撕裂强度(TD) | ASTM D-1922 | 15 | g/m | |
维卡软化点 | ASTM D-1525 | 105 | ℃ | |
脆化温度 | ASTM D-746 | ℃ | ||
薄膜厚度 | ASTM D-746 | 50 | m |